Sunstone is a transparent, eye-catching, orange
This glass works smoothly in a wide range of flame types, but usually a neutral flame is advised. It is a glass for those who are not put off by complicated kiln annealing, because although the color can develop with processing, it is not until a final annealing in the kiln that the full color will emerge.
The ideal orange color saturation occurs after 6 hours at 580°C. Similar results can be achieved at 4 h 594°C or 8 h 566°C. Overstriking can lead to more amber tones and some haze may occur in thick and/or heavily processed areas. Molten Aura recommends testing some small processed parts to determine what times and temperatures work best with your particular working style and kiln.
For best results, blowouts are preferable to coilpots.
Chemie, technologie en verbeelding smelten samen tot kleuren van de hoogste kwaliteit.
De processen en formules die bij Molten Aura Labs zijn ontwikkeld, zetten een nieuwe standaard voor de gekleurde borosilicaatmarkt. Het doel is om consequent sterk verzadigde borosilicaatglaskleuren van museumkwaliteit te maken.
De glaskleuren die in The Lab worden ontwikkeld, beginnen als siliciumdioxide. Dat silica wordt gecombineerd met hoogzuivere chemicaliën en vervolgens bij extreem hoge temperaturen tot glas gesmolten. Dit glas wordt tot staven getrokken met een diameter van ongeveer 6-9 mm.
Elk element dat in het glas gebruikt wordt, heeft op de een of andere manier invloed op de eigenschappen van het glas. Geen enkel gekleurd glas werkt precies zoals zijn transparante, heldere tegenhanger. Zelfs verschillende merken helder boro gedragen zich niet precies hetzelfde. Toch doet Molten Aura zijn uiterste best om ervoor te zorgen dat de balans van thermische uitzettingscoëfficiënt en viscositeit compatibel is met 33 COE Borosilicaat.